Interface of Spray-Deposited+Rolled Al-Ph/Al/Steel Composite Plate

HU Dunyan; YANG Bin; CUI Hua; DUAN Xianjin; ZHANG Jishan; XIONG Boqing

doi:10.13374/j.issn1001-053x.2001.04.014

Volume 23 Issue 4

Aug. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2001 > 23(4): 340-342

HU Dunyan, YANG Bin, CUI Hua, DUAN Xianjin, ZHANG Jishan, XIONG Boqing. Interface of Spray-Deposited+Rolled Al-Ph/Al/Steel Composite Plate[J]. Chinese Journal of Engineering, 2001, 23(4): 340-342. doi: 10.13374/j.issn1001-053x.2001.04.014

Citation:

HU Dunyan, YANG Bin, CUI Hua, DUAN Xianjin, ZHANG Jishan, XIONG Boqing. Interface of Spray-Deposited+Rolled Al-Ph/Al/Steel Composite Plate[J]. Chinese Journal of Engineering, 2001, 23(4): 340-342. doi: 10.13374/j.issn1001-053x.2001.04.014

Citation:

PDF( 499 KB)

Interface of Spray-Deposited+Rolled Al-Ph/Al/Steel Composite Plate

doi: 10.13374/j.issn1001-053x.2001.04.014

1. State Key Laboratory for Advanced Metals and Materials, UST Beijing Beijing 100083, China;
2. General Research Institute for Nonferrous Metals, Beijing 100088, China

Received Date: 2000-10-27

Abstract

Abstract

Heat treatment was conducted to spray-deposited+rolled Al-Ph/Al/steel composite plate. The morphology of the interfaces between Al-Ph and Al, and between Al and steel was observed by SEM. The experimental results showed that a good pre-cohesion in the interfaces after rolling. FeAl intermetallic, however, was found in the interface between Al and steel after heat treatment of 480℃/1h+300℃/3h.
- spray forming,
- Al-Ph/Al/steel composite plate,
- roll,
- interface