Detection of nonmetallic inclusion in high-strength gear steel with high cleanliness

XIAO Na; HUI Wei-jun; ZHANG Yong-jian; ZHAO Xiao-li; CHEN Ying

doi:10.13374/j.issn2095-9389.2019.07.15.005

Volume 42 Issue 7

Jul. 2020

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2020 > 42(7): 912-921

XIAO Na, HUI Wei-jun, ZHANG Yong-jian, ZHAO Xiao-li, CHEN Ying. Detection of nonmetallic inclusion in high-strength gear steel with high cleanliness[J]. Chinese Journal of Engineering, 2020, 42(7): 912-921. doi: 10.13374/j.issn2095-9389.2019.07.15.005

Citation:

XIAO Na, HUI Wei-jun, ZHANG Yong-jian, ZHAO Xiao-li, CHEN Ying. Detection of nonmetallic inclusion in high-strength gear steel with high cleanliness[J]. Chinese Journal of Engineering, 2020, 42(7): 912-921. doi: 10.13374/j.issn2095-9389.2019.07.15.005

Citation:

PDF( 1704 KB)

Detection of nonmetallic inclusion in high-strength gear steel with high cleanliness

doi: 10.13374/j.issn2095-9389.2019.07.15.005

1.
School of Mechanical, Electronic and Control Engineering, Beijing Jiaotong University, Beijing 100044, China
2.
Central Laboratory, Central Iron and Steel Research Institute, Beijing 100081, China

More Information

Corresponding author: E-mail: wjhui@bjtu.edu.cn
Received Date: 2019-07-15
Publish Date: 2020-07-01

Abstract

Abstract

It is well known that large-sized nonmetallic inclusion seriously affects the mechanical properties of high-strength steels, particularly the fatigue properties. Therefore, significant efforts have been made to enhance the fatigue properties of gear steels by improving the cleanliness and, thus, reducing the size and the number of inclusions in steels. However, an effective inclusion inspection method is particularly important because of the relatively low-rate emergence of large-sized inclusions in highly clean steels. Herein, a new inclusion inspection strategy was proposed using a properly hydrogen-charged tensile specimen combined with the application of the statistics of extreme value (SEV) method, which can be used to conveniently and reliably estimate the maximum inclusion size in any volume of high-strength steel and its fatigue strength. A commercial heat of 20Cr2Ni4A gear steel with high cleanliness was used to verify the proposed method. Standard tensile specimens were quenched, tempered at low-temperature, and then properly charged with electrochemical hydrogen. It is found that there were many embrittled platforms, generally with large inclusions on the fracture surfaces of the specimens after normal tensile testing because of the trapping of the charged hydrogen around inclusion and the occurrence of hydrogen embrittlement. The size, composition, and distribution of these inclusions can be analyzed using a scanning electron microscopy, thus, the maximum inclusion size can be predicted using the SEV method. To verify the accuracy of the proposed method, additional inclusion rating methods of conventional optical metallographic observation and high-cycle fatigue testing were conducted. Using the proposed method, it was confirmed that the predicted maximum inclusion size and fatigue strength are consistent with that obtained via the rotating bending fatigue test. Therefore, the proposed method is a promising, efficient, and reliable for use in high-strength steels with high cleanliness to inspect the maximum size inclusion and predict fatigue strength.
- assessment of the maximum inclusion size,
- hydrogen embrittlement,
- statistics of extreme value method,
- gear steel,
- high cleanliness steel

FullText(HTML)

References(27)

References

[1]	Savaria V, Bridier F, Bocher P. Predicting the effects of material properties gradient and residual stresses on the bending fatigue strength of induction hardened aeronautical gears. Int J Fatigue, 2016, 85: 70 doi: 10.1016/j.ijfatigue.2015.12.004
[2]	Jo B, Sharifimehr S, Shim Y, et al. Cyclic deformation and fatigue behavior of carburized automotive gear steel and predictions including multiaxial stress states. Int J Fatigue, 2017, 100: 454 doi: 10.1016/j.ijfatigue.2016.12.023
[3]	Nehila A, Li W, Gao N, et al. Very high cycle fatigue of surface carburized CrNi steel at variable stress ratio: failure analysis and life prediction. Int J Fatigue, 2018, 111: 112 doi: 10.1016/j.ijfatigue.2018.02.006
[4]	Liu P F, Li W, Nehila A, et al. High cycle fatigue property of carburized 20Cr gear steel under axial loading. Metals, 2016, 6(10): 246 doi: 10.3390/met6100246
[5]	Mengaroni S, Bambach M D, Cianetti F, et al. Strengthening improvement on gear steels. Steel Res Int, 2016, 87(5): 608 doi: 10.1002/srin.201500155
[6]	Dong W L, Ni H W, Zhang H, et al. Effect of slag composition on the cleanliness of 28MnCr5 gear steel in the refining processes. Int J Miner Metall Mater, 2016, 23(3): 269 doi: 10.1007/s12613-016-1235-y
[7]	Murakami Y, Kodama S, Konuma S. Quantitative evaluation of effects of non-metallic inclusions on fatigue strength of high strength steels. I: basic fatigue mechanism and evaluation of correlation between the fatigue fracture stress and the size and location of non-metallic inclusions. Int J Fatigue, 1989, 11(5): 291 doi: 10.1016/0142-1123(89)90054-6
[8]	Atkinson H V, Shi G. Characterization of inclusions in clean steels: a review including the statistics of extremes methods. Prog Mater Sci, 2003, 48(5): 457 doi: 10.1016/S0079-6425(02)00014-2
[9]	Bartosiaki B G, Pereira J A M, Bielefeldt W V, et al. Assessment of inclusion analysis via manual and automated SEM and total oxygen content of steel. J Mater Res Technol, 2015, 4(3): 235 doi: 10.1016/j.jmrt.2015.01.008
[10]	Yu H X, Shao X J, Zhang J, et al. Study on the quantitative relationship between total oxygen content and non-metallic inclusion in steel with ASPEX SEM. Chin J Eng, 2015, 37(增刊1): 35 于會香, 邵肖靜, 張靜, 等. 采用ASPEX掃描電鏡研究鋼中總氧和非金屬夾雜物的定量關系. 工程科學學報, 2015, 37(增刊1):35)
[11]	Furuya Y, Matsuoka S, Abe T. A novel inclusion inspection method employing 20 kHz fatigue testing. Metall Mater Trans A, 2003, 34(11): 2517 doi: 10.1007/s11661-003-0011-6
[12]	Zhang J M, Zhang J F, Yang Z G, et al. Estimation of maximum inclusion size and fatigue strength in high-strength ADF1 steel. Mater Sci Eng A, 2005, 394(1-2): 126 doi: 10.1016/j.msea.2004.11.015
[13]	Shi G, Atkinson H V, Sellars C M, et al. Maximum inclusion size in two clean steels Part 2 use of data from cold crucible remelted samples and polished optical cross-sections. Ironmaking Steelmaking, 2000, 27(5): 361 doi: 10.1179/030192300677660
[14]	楊振國, 張繼明, 李守新, 等. 高周疲勞條件下高強鋼臨界夾雜物尺寸估算. 金屬學報, 2005, 41(11):1136 doi: 10.3321/j.issn:0412-1961.2005.11.004 Yang Z G, Zhang J M, Li S X, et al. Estimation of the critical size of inclusion in high strength steel under high cycle fatigue condition. Acta Metall Sin, 2005, 41(11): 1136 doi: 10.3321/j.issn:0412-1961.2005.11.004
[15]	Fujita S, Murakami Y. A new nonmetallic inclusion rating method by positive use of hydrogen embrittlement phenomenon. Metall Mater Trans A, 2013, 44(1): 303 doi: 10.1007/s11661-012-1376-1
[16]	Hui W J, Xu Z B, Zhang Y J, et al. Hydrogen embrittlement behavior of high strength rail steels: A comparison between pearlitic and bainitic microstructure. Mater Sci Eng A, 2017, 704: 199 doi: 10.1016/j.msea.2017.08.022
[17]	Wang C, Petit J, Huang Z Y, et al. Investigation of crack initiation mechanisms responsible for the fish eye formation in the very high cycle fatigue regime. Int J Fatigue, 2019, 119: 320 doi: 10.1016/j.ijfatigue.2018.06.016
[18]	Zhu M L, Jin L, Xuan F Z. Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes. Acta Mater, 2018, 157: 259 doi: 10.1016/j.actamat.2018.07.036
[19]	Bhadeshia H K D H. Prevention of hydrogen embrittlement in steels. ISIJ Int, 2016, 56(1): 24 doi: 10.2355/isijinternational.ISIJINT-2015-430
[20]	Otsuka T, Hanada H, Nakashima H, et al. Observation of hydrogen distribution around non-metallic inclusions in steels with tritium microautoradiography. Fusion Sci Technol, 2005, 48(1): 708 doi: 10.13182/FST05-A1022
[21]	Takai K, Seki J I, Homma Y. Observation of trapping sites of hydrogen and deuterium in high-strength steels by using secondary ion mass spectrometry. Mater Trans JIM, 1995, 36(9): 1134 doi: 10.2320/matertrans1989.36.1134
[22]	褚武揚, 喬利杰, 李金許, 等. 氫脆和應力腐蝕. 北京: 科學出版社, 2013 Chu W Y, Qiao L J, Li J X, et al. Hydrogen Embrittlement and Stress Corrosion Cracking. Beijing: Science Press, 2013
[23]	Han J, Nam J H, Lee Y K. The mechanism of hydrogen embrittlement in intercritically annealed medium Mn TRIP steel. Acta Mater, 2016, 113: 1 doi: 10.1016/j.actamat.2016.04.038
[24]	Qi Y M, Luo H Y, Zheng S Q, et al. Effect of immersion time on the hydrogen content and tensile properties of A350LF2 steel exposed to hydrogen sulphide environments. Corros Sci, 2013, 69: 164 doi: 10.1016/j.corsci.2012.11.038
[25]	Todoshchenko O M I, Yagodzinskyy Y, Saukkonen T, et al. Role of nonmetallic inclusions in hydrogen embrittlement of high-strength carbon steels with different microalloying. Metall Mater Trans A, 2014, 45(11): 4742 doi: 10.1007/s11661-014-2447-2
[26]	Genel K. Estimation method for the fatigue limit of case hardened steels. Surf Coat Technol, 2005, 194(1): 91 doi: 10.1016/j.surfcoat.2004.04.077
[27]	Liu Y B, Li Y D, Li S X, et al. Prediction of the S-N curves of high-strength steels in the very high cycle fatigue regime. Int J Fatigue, 2010, 32(8): 1351 doi: 10.1016/j.ijfatigue.2010.02.006