NaCl Type fcc Cr Carbide Formation

Wang Jian; Fang Zhengzhi

doi:10.13374/j.issn1001-053x.1992.04.030

Volume 14 Issue 4

Oct. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 1992 > 14(4): 478-482

Wang Jian, Fang Zhengzhi. NaCl Type fcc Cr Carbide Formation[J]. Chinese Journal of Engineering, 1992, 14(4): 478-482. doi: 10.13374/j.issn1001-053x.1992.04.030

Citation:

Wang Jian, Fang Zhengzhi. NaCl Type fcc Cr Carbide Formation[J]. Chinese Journal of Engineering, 1992, 14(4): 478-482. doi: 10.13374/j.issn1001-053x.1992.04.030

Wang Jian, Fang Zhengzhi. NaCl Type fcc Cr Carbide Formation[J]. Chinese Journal of Engineering, 1992, 14(4): 478-482. doi: 10.13374/j.issn1001-053x.1992.04.030

Citation:

Wang Jian, Fang Zhengzhi. NaCl Type fcc Cr Carbide Formation[J]. Chinese Journal of Engineering, 1992, 14(4): 478-482. doi: 10.13374/j.issn1001-053x.1992.04.030

PDF( 830 KB)

NaCl Type fcc Cr Carbide Formation

doi: 10.13374/j.issn1001-053x.1992.04.030

Department of Materials phgsics

Received Date: 1991-10-29
Available Online: 2021-10-16

Abstract

Abstract

A simple fcc Cr carbide was formed for the firal time by carbon ion implantation into Cr thin filma. Lattice constant determined by electron diffraction was 0.403nm. In situ annealing in TEM showed it exited upto a temperature about 250℃. The carbide phase was further confirmed by Auerg electron spectra. The meidema heat of formation was - 29.4kJ/mbl.
- ion implanlation phase,
- heat of formation,
- CrC,