Low-temperature selective catalytic reduction of NOz and anti-toxicity of MnOx?FeOy/TiO2?ZrO2?CeO2

ZHANG Qing; HE Shuan-ling; ZHANG Zheng; WANG Li

doi:10.13374/j.issn2095-9389.2019.11.05.002

Volume 42 Issue 3

Mar. 2020

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2020 > 42(3): 321-330

ZHANG Qing, HE Shuan-ling, ZHANG Zheng, WANG Li. Low-temperature selective catalytic reduction of NOz and anti-toxicity of MnOx?FeOy/TiO2?ZrO2?CeO2[J]. Chinese Journal of Engineering, 2020, 42(3): 321-330. doi: 10.13374/j.issn2095-9389.2019.11.05.002

Citation:

ZHANG Qing, HE Shuan-ling, ZHANG Zheng, WANG Li. Low-temperature selective catalytic reduction of NO_z and anti-toxicity of MnO_x?FeO_y/TiO₂?ZrO₂?CeO₂[J]. Chinese Journal of Engineering, 2020, 42(3): 321-330. doi: 10.13374/j.issn2095-9389.2019.11.05.002

Citation:

PDF( 1172 KB)

Low-temperature selective catalytic reduction of NO_z and anti-toxicity of MnO_x?FeO_y/TiO₂?ZrO₂?CeO₂

doi: 10.13374/j.issn2095-9389.2019.11.05.002

1.
School of Energy and Environment Engineering, University of Science and Technology Beijing, Beijing 100083, China
2.
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

More Information

Corresponding author: E-mail: wangli@ces.ustb.edu.cn
Received Date: 2019-11-05
Publish Date: 2020-03-01

Abstract

Abstract

One of the most effective methods for the removal of NO_z from industrial flue gas is the technology known as low-temperature selective catalytic reduction (SCR). The main problem limiting the industrial application of catalysts is the need to improve their performances at low temperatures, and the fact that the anti-toxic mechanism of low-temperature denitration catalysts has yet to be explicitly identified. In this study, a TiO₂?ZrO₂?CeO₂ (molar ratio 4∶1∶1.25) carrier was prepared by the sol–gel method, and then loaded the active components MnO_x and MnO_x?FeO_y using the citric-acid-solution impregnation method to synthesize a new type of Fe-modified Mn-based multi-oxidation-state composite catalyst. The performance of this Mn-based composite oxide catalyst was investigated with respect to its NH₃-selective catalytic reduction of NO and sulfur resistance. The catalyst exhibits good low-temperature SCR redox ability and anti-poisoning ability in an SO₂-containing atmosphere, whereby the introduction of Fe promotes the interaction between Mn and the TiO₂?ZrO₂?CeO₂ (4∶1∶1.25) carrier, and increases the number of Lewis acid sites on the catalyst surface. According to the XPS analysis, the contents of Mn⁴⁺, Ce⁴⁺, and adsorbed oxygen are obviously increased, which is very advantageous for improving the performance of the catalyst. According to the thermogravimetric analysis, the introduction of Fe reduces the production of ammonium sulfate and ceric sulfate in the atmosphere containing SO₂ and H₂O, and inhibites the sulfation of manganese. The Fe element thereby increases the anti-toxic ability of the Mn-based multi-oxidation-state composite catalyst. By maintaining the MnO_x (12.5%)?FeO_y(0.8)/TiO₂?ZrO₂?CeO₂ (4∶1∶1.25) catalyst at 180 ℃, while continuously feeding 10% H₂O in volume fraction and 125×10^?6 SO₂ for 240 min, the NO_z conversion rate can be stably maintained at 75.6%. Based on the results of this work, a new type of Mn-based composite oxide catalyst has been developed that provides a foundation for further exploring the SCR reaction of the catalyst and its anti-toxic mechanism to promote the industrial application of the SCR process.
- MnO_x?FeO_y/TiO₂?ZrO₂?CeO₂,
- selective catalytic reduction,
- nitrogen oxides,
- low temperature,
- sulfur resistance

FullText(HTML)

References(27)

References

[1]	Gao R H, Zhang D S, Liu X G, et al. Enhanced catalytic performance of V₂O₅-WO₃/Fe₂O₃/TiO₂ microspheres for selective catalytic reduction of NO by NH₃. Catal Sci Technol, 2013, 3(1): 191
[2]	王麗秋, 王小方, 李會泉, 等. 焦爐煙氣濕法鋼渣聯合脫硫脫硝工藝及機理研究. 燕山大學學報, 2016, 40(4):348 doi: 10.3969/j.issn.1007-791X.2016.04.009 Wang L Q, Wang X F, Li H Q, et al. Research on technical method and mechanism of combined desulfurization and denitrification of flue gas from coking furnace with steel slag. J Yanshan Univ, 2016, 40(4): 348 doi: 10.3969/j.issn.1007-791X.2016.04.009
[3]	Liu Z, Zhang S, Junhua L I, et al. Novel V₂O₅-CeO₂/TiO₂ catalyst with low vanadium loading for the selective catalytic reduction of NO_x by NH₃. Appl Catal B Environ, 2014, 158-159(3): 11
[4]	Tang X F, Li J H, Sun L, et al. Origination of N₂O from NO reduction by NH₃ over β-MnO₂ and α-Mn₂O₃. Appl Catal B Environ, 2010, 99(1-2): 156
[5]	France L J, Yang Q, Li W, et al. Ceria modified FeMnO_x?Enhanced performance and sulphur resistance for low-temperature SCR of NO_x. Appl Catal B Environ, 2017, 206: 203
[6]	Qiu M Y, Zhan S H, Zhu D D, et al. NH₃-SCR performance improvement of mesoporous Sn modified Cr-MnOx catalysts at low temperatures. Catal Today, 2015, 258: 103
[7]	Chang H Z, Li J H, Chen X Y, et al. Effect of Sn on MnO_x-CeO₂ catalyst for SCR of NO_x by ammonia: Enhancement of activity and remarkable resistance to SO₂. Catal Commun, 2012, 27: 54
[8]	Guo Y H, Wei H Y, Zhao G Y, et al. Low temperature catalytic performance of coal-fired flue gas oxidation over Mn?Co?Ce?O_x. Fuel, 2017, 206: 318
[9]	Fang N J, Guo J X, Shu S, et al. Enhancement of low-temperature activity and sulfur resistance of Fe_0.3Mn_0.5Zr_0.2 catalyst for NO removal by NH₃-SCR. Chem Eng J, 2017, 325: 114
[10]	Wu Z B, Jiang B Q, Liu Y, et al. Experimental study on a low-temperature SCR catalyst based on MnO_x/TiO₂ prepared by sol-gel method. J Hazard Mater, 2007, 145(3): 488
[11]	Qi G, Yang R T. Low-temperature selective catalytic reduction of NO with NH₃ over iron and manganese oxides supported on titania. Appl Catal B Environ, 2003, 44(3): 217
[12]	Fang C, Zhang D S, Shi L Y, et al. Highly dispersed CeO₂ on carbon nanotubes for selective catalytic reduction of NO with NH₃. Catal Sci Technol, 2013, 3(3): 803
[13]	Jin R B, Liu Y, Wang Y, et al. The role of cerium in the improved SO₂ tolerance for NO reduction with NH₃ over Mn-Ce/TiO₂ catalyst at low temperature. Appl Catal B Environ, 2014, 148-149: 582
[14]	李強. MnO_x/TiO₂?ZrO₂?CeO₂催化劑的低溫SCR脫硝性能和抗毒性研究[學位論文]. 北京: 北京科技大學, 2017 Li Q. Activity and Antitoxic Properties of MnO_x/TiO₂?ZrO₂?CeO₂ for the Low-Temperature Selective Catalytic Reduction of NO [Dissertation]. Beijing: University of Science and Technology Beijing, 2017
[15]	徐海迪, 邱春天, 張秋林, 等. WO₃對MnO_x?CeO₂/ZrO₂?TiO₂整體式催化劑NH₃選擇性催化還原NO_x性能的影響. 物理化學學報, 2010, 26(9):2449 doi: 10.3866/PKU.WHXB20100838 Xu H D, Qiu C T, Zhang Q L, et al. Influence of tungsten oxide on selective catalytic reduction of NO_x with NH₃ over MnO_x?CeO₂/ZrO₂?TiO₂ monolith catalyst. Acta Phys-Chim Sin, 2010, 26(9): 2449 doi: 10.3866/PKU.WHXB20100838
[16]	鐘標城, 周廣英, 王文輝, 等. Fe摻雜對MnO_x催化劑結構性質及低溫SCR反應機制的影響. 環境科學學報, 2011, 31(10):2091 Zhong B C, Zhou G Y, Wang W H, et al. The effects of Fe substitution on the structure of MnO_x catalyst and reaction pathway for low temperature SCR. Acta Sci Circum, 2011, 31(10): 2091
[17]	Chen Z, Yang Q, Li H, et al. Cr-MnO_x mixed-oxide catalysts for selective catalytic reduction of NO_x with NH₃ at low temperature. J Catalysis, 2010, 276(1): 56
[18]	Ettireddy P R, Ettireddy N, Mamedov S, et al. Surface characterization studies of TiO₂ supported manganese oxide catalysts for low temperature SCR of NO with NH₃. Appl Catal B Environ, 2007, 76(1-2): 123
[19]	郭家秀, 袁書華, 龔茂初, 等. Ce_0.35Zr_0.55La_0.10O_1.95對低貴金屬Pt?Rh型三效催化劑性能的影響. 物理化學學報, 2007, 23(1):73 Guo J X, Yuan S H, Gong M C, et al. Influence of Ce_0.35Zr_0.55La_0.10O_1.95 solid solution on the performance of Pt-Rh three-way catalysts. Acta Phys-Chim Sin, 2007, 23(1): 73
[20]	Zieliński J, Zglinicka I, Znak L, et al. Reduction of Fe₂O₃ with hydrogen. Appl Catal A General, 2010, 381(1-2): 191
[21]	Xu H D, Wang Y, Cao Y, et al. Catalytic performance of acidic zirconium-based composite oxides monolithic catalyst on selective catalytic reduction of NO_x with NH₃. Chem Eng J, 2014, 240: 62
[22]	張秋林, 林濤, 李偉, 等. MnO₂?CeO₂/Ti_0.25Zr_0.25Al_0.5O_1.75整體式催化劑的低溫NH₃選擇性催化還原NO性能研究. 無機化學學報, 2009, 25(3):485 doi: 10.3321/j.issn:1001-4861.2009.03.020 Zhang Q L, Lin T, Li W, et al. Catalytic performance of MnO₂?CeO₂/Ti_0.25Zr_0.25Al_0.5O_1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH₃. Chin J Inorg Chem, 2009, 25(3): 485 doi: 10.3321/j.issn:1001-4861.2009.03.020
[23]	范蕓珠, 曹發海. 硫酸銨熱分解反應動力學研究. 高校化學工程學報, 2011, 25(2):341 doi: 10.3969/j.issn.1003-9015.2011.02.028 Fan Y Z, Cao F H. Thermal decomposition kinetics of ammonium sulfate. J Chem Eng Chin Univ, 2011, 25(2): 341 doi: 10.3969/j.issn.1003-9015.2011.02.028
[24]	Li X S, Yang G S, Wu W Y, et al. Study on roast reaction kinetics and crystal behavior of Ceria-based rare earth polishing powder. J Rare Earths, 2007, 25: 134
[25]	蔡鑫. 硫鐵化合物低溫氧化過程及動力學研究[學位論文]. 鄭州: 鄭州大學, 2015 Cai X. Study on the Iron Sulfide Oxidation Process and Kinetics under Low Temperatures[Dissertation]. Zhengzhou: Zhengzhou University, 2015
[26]	張愛華. 錳化合物的熱分解動力學[學位論文]. 武漢: 中國地質大學, 2010 Zhang A H. Kinetics for Thermal Decomposition of Manganese Compounds[Dissertation]. Wuhan: China University of Geosciences, 2010
[27]	Sheng Z Y, Hu Y F, Xue J M, et al. A novel co-precipitation method for preparation of Mn-Ce/TiO₂ composites for NO_x reduction with NH₃ at low temperature. Environ Technol, 2012, 33(21): 2421