Study on the enrichment behavior of phosphorus in high phosphorus converter slag

WANG Da-zhi; BAO Yan-ping; WANG Min

doi:10.13374/j.issn2095-9389.2018.s1.010

Volume 40 Issue S1

Dec. 2018

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2018 > 40(S1): 65-72

WANG Da-zhi, BAO Yan-ping, WANG Min. Study on the enrichment behavior of phosphorus in high phosphorus converter slag[J]. Chinese Journal of Engineering, 2018, 40(S1): 65-72. doi: 10.13374/j.issn2095-9389.2018.s1.010

Citation:

WANG Da-zhi, BAO Yan-ping, WANG Min. Study on the enrichment behavior of phosphorus in high phosphorus converter slag[J]. Chinese Journal of Engineering, 2018, 40(S1): 65-72. doi: 10.13374/j.issn2095-9389.2018.s1.010

Citation:

PDF( 1045 KB)

Study on the enrichment behavior of phosphorus in high phosphorus converter slag

doi: 10.13374/j.issn2095-9389.2018.s1.010

State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing

Received Date: 2017-10-15
Available Online: 2023-07-18

Abstract

Abstract

In order to realize the effective enrichment of phosphorus in high phosphorus converter slag, using the Ca O-Si O₂-Fe₂O₃-P₂O₅-MgO-MnO slag with a P₂O₅content of 10% (mass fraction) as the research object, the form of phosphorus in the high phosphorous slag was studied by the laboratory hot state experiment.The effects of basicity and Fe₂O₃content on the enrichment of phosphorus in high phosphorus converter slag were investigated.The results show that the phosphorus element in the high phosphorus converter slag mainly exists in the form of n2CaO·Si O₂-3CaO·P₂O₅ (n C₂S-C₃P) solid solution and the changes of slag basicity and Fe₂O₃content have no effect on the phosphorus occurrence form.The change of basicity has an effect on the production of 2CaO·Si O₂.Too high or too low basicity is not conducive to the enrichment of phosphorus from slag to phosphorus-rich phase.Controlling the slag basicity in the range of 1.5-1.8 is conducive to the full enrichment of phosphorus in slag.Increasing the Fe₂O₃content in the slag can reduce the precipitation of 2CaO·Si O₂and increase the content of P₂O₅in the phosphorus-rich phase, which is favorable for the enrichment of phosphorus in the slag.
- converter slag,
- basicity,
- iron oxide,
- phosphorus,
- enrichment

FullText(HTML)

References(16)

References

[1]	Yao C X, Liao H Q, Son H P, et al. Physicochemical properties of steel slag ultra-fine power. J Iron Steel Res, 2017, 29 (3) :195 (姚晨星, 廖洪強, 宋慧平, 等.鋼渣超微粉理化特性.鋼鐵研究學報, 2017, 29 (3) :195)
[2]	Akin Altun I, Yilmaz I. Study on steel furnace slags with high Mg O as additive in portland cement. Cem Concr Res, 2002, 32 (8) :1247
[3]	Tian J L, Zhang Q. Resource utilization of steel slag and environmental pollution treatment. Resour Recycl, 2013 (1) :55 (田京累, 張倩.鋼渣在環境污染治理中的資源化利用.資源再生, 2013 (1) :55)
[4]	Gao B H, Hao Y D, Zhang S L, et al. Development trend and comprehensive utilization of steel slag. Environ Eng, 2016, 34 (s1) :776 (高本恒, 郝以黨, 張淑苓, 等.鋼渣綜合利用現狀及發展趨勢.環境工程, 2016, 34 (s1) :776)
[5]	Wu L, Hao Y D, Yue C S, et al. Current situation and discussion of steel slag utilization technology. Ind Saf Environ Prot, 2016, 42 (9) :99 (吳龍, 郝以黨, 岳昌盛, 等.鋼渣資源化利用現況和探討.工業安全與環保, 2016, 42 (9) :99)
[6]	Zhang W, Liu W X, Li J, et al. Main factors of gasification dephosphorization of high phosphorus steel slag. Iron Steel, 2015, 50 (1) :11 (張偉, 劉衛星, 李杰, 等.高磷鋼渣氣化脫磷影響因素的實驗.鋼鐵, 2015, 50 (1) :11)
[7]	Wang Y C, Li H Y, Li S W, et al. Thermodynamic analysis and experiment ongasification dephosphorization reaction of converter slag. J Iron Steel Res, 2016, 28 (6) :31 (王藝慈, 李海洋, 李雙威, 等.轉爐鋼渣氣化脫磷反應的熱力學分析及試驗.鋼鐵研究學報, 2016, 28 (6) :31)
[8]	Zhong M, Matsuura H, Tsukihashi F. Activity of phosphorus pentoxide and tri-calcium phosphate in 2CaO·SiO2--3CaO·P2O5solid solution saturated with CaO. Mater Trans, 2015, 56 (8) :1192
[9]	Lin L, Bao Y P, Yang Q, et al. Effect of CaF2and SiO2modification on phosphorus utilization in P-bearing slag. Ironmaking Steelmaking, 2015, 42 (5) :331
[10]	Xie S, Wang W, Liu Y, et al. Effect of Na2O and B2O3on the distribution of P2O5between solid solution and liquid phases slag. ISIJ Int, 2014, 54 (4) :766
[11]	Suito H, Inoue R. Behavior of phosphorus transfer from CaO--FetO--P2O5 (--SiO2) slag to CaO particles. ISIJ Int, 2006, 46 (2) :180
[12]	Yang X, Matsuura H, Tsukihashi F. Condensation of P2O5at the interface between 2CaO·SiO2and CaO--SiO2--Fe Ox--P2O5slag.ISIJ Int, 2009, 49 (9) :1298
[13]	LI J Y, Zhang M, Guo M, et al. Enrichment mechanism of phosphate in CaO--SiO2-Fe O-Fe2O3--P2O5steelmaking slags. Metall Mater Trans B, 2014, 45 (5) :1666
[14]	LI J Y, Zhang M, Guo M, et al. Phosphate enrichment mechanism in CaO-Si O2-Fe O-Fe2O3--P2O5steelmaking slags with lower binary. Int J Miner Metall Mater, 2016, 23 (5) :520
[15]	Jiang L, Diao J, Xie B, et al. Effect of Al2O3on enrichment of phosphorus in hot metal dephosphorization slag. ISIJ Int, 2015, 55 (3) :564
[16]	Lin L, Bao Y P, Wang M, et al. Influence of tatania modification on phosphorus enrichment in P-bearing steelmaking slag. J Univ Sci Technol Beijing, 2014, 36 (8) :1013 (林路, 包燕平, 王敏, 等.二氧化鈦改質對含磷轉爐渣中磷富集行為的影響.北京科技大學學報, 2014, 36 (8) :1013)