Analysis on the surface temperature of a beam blank

LIU Jianhua; BAO Yanping; CHEN Gaoxing; DU Songlin; SUN Wei; HUANG Sheqing

doi:10.13374/j.issn1001-053x.2005.06.008

Volume 27 Issue 6

Aug. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2005 > 27(6): 671-674

LIU Jianhua, BAO Yanping, CHEN Gaoxing, DU Songlin, SUN Wei, HUANG Sheqing. Analysis on the surface temperature of a beam blank[J]. Chinese Journal of Engineering, 2005, 27(6): 671-674. doi: 10.13374/j.issn1001-053x.2005.06.008

Citation:

LIU Jianhua, BAO Yanping, CHEN Gaoxing, DU Songlin, SUN Wei, HUANG Sheqing. Analysis on the surface temperature of a beam blank[J]. Chinese Journal of Engineering, 2005, 27(6): 671-674. doi: 10.13374/j.issn1001-053x.2005.06.008

Citation:

PDF( 503 KB)

Analysis on the surface temperature of a beam blank

doi: 10.13374/j.issn1001-053x.2005.06.008

1. Metalluigical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083, China;
2. Maanshan Iron and Steel Co. Ltd., Maanshan 243000, China

Received Date: 2004-10-18
Rev Recd Date: 2004-11-05

Available Online: 2021-08-17

Abstract

Abstract

The surface temperature of an SS400 beam blank was measured with an CIT-M Infrared Pyrometer and the hot ductility of SS400 steel was tested in a Gleeble-2000 thermomechanical simulator. The results showed that the surface temperatures of the SS400 beam blank in the secondary cooling area and at the straightening places were normally in 760-880℃, i.e., the fragile temperature range of SS400 steel. The rebounds of surface temperature between some supporting rollers in the second segment of secondary cooling area, caused by discontinuously water spraying, were higher than the permitted range 100℃ ·m^-1 according to the metallurgical rules for secondary cooling.
- beam blank,
- surface temperature,
- continuous casting,
- hot-rolling