Microstructure of Long Time Aging in GH169 Alloys

Dong Jianxin; Bai Yuanqiang; Xu Zhichao; Xie Xishan; Zhang Shouhua

doi:10.13374/j.issn1001-053x.1993.06.005

Volume 15 Issue 6

Oct. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 1993 > 15(6): 567-571

Dong Jianxin, Bai Yuanqiang, Xu Zhichao, Xie Xishan, Zhang Shouhua. Microstructure of Long Time Aging in GH169 Alloys[J]. Chinese Journal of Engineering, 1993, 15(6): 567-571. doi: 10.13374/j.issn1001-053x.1993.06.005

Citation:

Dong Jianxin, Bai Yuanqiang, Xu Zhichao, Xie Xishan, Zhang Shouhua. Microstructure of Long Time Aging in GH169 Alloys[J]. Chinese Journal of Engineering, 1993, 15(6): 567-571. doi: 10.13374/j.issn1001-053x.1993.06.005

Citation:

PDF( 1527 KB)

Microstructure of Long Time Aging in GH169 Alloys

doi: 10.13374/j.issn1001-053x.1993.06.005

Department of Materials Science and Engineering

Received Date: 1993-06-21
Available Online: 2021-10-18

Abstract

Abstract

Microstructure after long time aging have been observed by means of SEM in GH169 alloys. The results show that the microstructure almost no variation after long time aging up to 5×10⁴h below 650℃, and reveals higher structure stability. However, microstructure is very sensitive to aging temperature beyond 650℃, and there existed complicated phase transformation. The experimental results also show that stress accelerates the complicated phase transformation by observing GH169 gas turbine disk with an engine service life of 2.8×10⁴h
- superalloy,
- aging,
- δ-phase,
- precipitation hardening/GH169,
- long time aging